What is the difference between 3003 and 6061 aluminum?

Although 3003 is about 20% stronger than pure aluminum, it is noticeably weaker than 6061. Additionally, 3003 is somewhat soft, making it more difficult to machine and vulnerable to scratches. This material has a H22 temper meaning it has been strain-hardened and partially annealed.

What does H14 mean in aluminum?

temper
It is used for drawing, forming, spinning, fuel tanks, sheet metal works and other applications that require moderate strength for an aluminum with good weldability. H14 designates the temper, and means that 3003 has been strain hardened and partially annealed.

What is 3003 Aluminium alloy used for?

Common end-uses for 3003 aluminum include cooking utensils, food containers, chemical equipment, pressure vessels, general sheet metal fabrication, hardware, tanks, and cabinets.

Is T6 aluminum stronger than steel?

Mild steel is slightly harder than 6061-T6, but the aluminum’s ability to flex under impact actually results in superior performance under impact loading. All of our Miracle Line of products have been engineered to provide equivalent or superior performance to their steel counterparts.

How strong is 3003 aluminum?

The tensile yield strength for 3003 aluminum alloy is 186 MPa (27,000 psi) and the ultimate strength is 200MPa (29,000 psi), which makes 3003 aluminum a moderately strong material.

What is the difference between H14 and H24?

There are a couple differences between 3003 H14 and 3105 H24. One of them is the Brinell Hardness; 3003 H14 has 42 BHN and 3105 H24 has 47 BHN. Another difference is the Fatigue Strength; 3003 H14 has only 60 MPa, whereas 3105 H24 has 74 MPa. In the alloy composition, 3003 H14 contains more Magnesium than 3105 H24.

What is H111 temper?

Temper Types H111 – Some work hardening imparted by shaping processes but less than required for H11 temper. H32 – Work hardened by rolling then stabilised by low-temperature heat treatment to quarter hard.

Can you bend 3003 aluminum?

Aluminium alloy 3003 excellent for bending The best series for forming – and thus for bending – are the alloy series 3xxx, 5xxx and in some cases 6xxx. Aluminium alloy 6063 is a good choice, for example, while 6082 is more difficult. Aluminium alloy 3003.

How strong is 6061 T6 aluminum?

6061-T6. T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.

How strong is aluminum angle iron?

6061 Aluminum is the most commonly used Aluminum Alloy. 6061 is highly rated for strength, almost twice that of 6063 and is generally used for structural applications where material strength is a significant factor….Product Description:

Properties
Tensile Strength, psi	45,000
Rockwell Hardness	B60

What is the difference between A6061 T6 and 3003 aluminum?

A6061 aluminum features higher strength (tensile strength range is 20 to 42 KSI) compared with 3003 aluminum. 6061 T6 is one of the most common materials in the world. The T6 refers to the temper or degree of hardness, which is achieved by precipitation hardening. This grade has a good strength-to-weight ratio and is also heat-treatable.

Is 6061 aluminum stronger than 3003 aluminum?

The increased strength of 6061 aluminum is a consequence of its alloying elements (magnesium/silicon), as well as its ability to be heat-treated. If strength is a major concern, look no further than 6061 aluminum; it is a strong, more resistant alternative to mild steels and is decidedly stronger than 3003 aluminum.

Is 6061 T6 stronger than steel?

Because of this, it has higher strength and hardness than base 6061. It has a high strength to weight ratio, making 6061-T6 an excellent alternative to Steel or Stainless Steel. 6061 is the most frequently used structural alloy and the most versatile of the heat-treatable aluminum alloys. Also, it has excellent machinability.

What is the workability of 3003 aluminum?

3003 aluminum has excellent workability, weldability and corrosion resistance, and conforms to AMS QQ-A-250/2 and ASTM B209. How does aluminum 3003 compare with another commonly used grade: 6061 aluminum?