What is the hardness of 17-4 stainless steel?
The mechanical properties of annealed grade 17-4 stainless steel are displayed in the following table….Mechanical Properties.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Hardness, Brinell | 352 | 352 |
| Hardness, Knoop (estimated from Rockwell C) | 363 | 363 |
What is the hardness of 17-4 Condition A?
The annealing (solution treatment) temperature is 1900° F, followed by air cooling. Maximum Brinell hardness at mid-radius is 363.
What is the Rockwell hardness of 17-4 H900?
190,000
17-4 PH Stainless Steel Properties
| Condition | Ultimate Tensile Strength (PSI) | Hardness Rockwell |
|---|---|---|
| H900 | 190,000 | C40 |
| H1025 | 155,000 | C35 |
| H1075 | 145,000 | C32 |
| H1150 | 135,000 | C28 |
How hard can you heat treat 17-4?
Alloy 17-4 can be heat treated to a variety of temperatures to develop a wide range of properties. Its mechanical properties can be optimized with heat treatment where very high yield strength up to 180 ksi can be achieved. Alloy 17-4 should not be used at temperatures above 572°F or at very low temperatures.
What is the difference between 17-4 and 17 4ph?
Type 17-4 PH provides an outstanding combination of high strength, good corrosion resistance, and good mechanical properties at temperatures up to 600°F (316°C). 17-4 PH has slightly more Ferrite than other PH grades, making it a bit more magnetic.
What type of steel is 17-4?
stainless steel
17-4 stainless steel, also known as SAE Type 630, is a common and exceptionally durable type of steel used in a diverse variety of industries and applications. The numbers “17-4” refer to its composition: ≈17% chromium and ≈4% nickel. It also can include between 3 and 5% copper.
What type of steel is 17-4 PH?
martensitic stainless steel
17-4 PH Stainless Steel is a precipitation hardening martensitic stainless steel. Typical usage is seen in applications requiring high strength and a modest level of corrosion resistance. Strength and toughness desired can be manipulated by temperate range in the heat treatment process.
What is the hardness of 416 stainless steel?
330
416 Martensitic Stainless Steel Bar
| Chemical Composition | |
|---|---|
| Max % | |
| Hardness | 330 |
| 36 | |
| High tensile strength and high yield strength but low impact properties when tempered below 400oC.*Note drop in impact properties.Tempering within the range 400oC – 580oC should be avoided. |
Can you heat treat 17 4 stainless steel?
The ATI 17-4™ precipitation hardening stainless steel is furnished in the annealed condition. This is also called the solution heat treated condition, or Condition A. Annealing is conducted by heat treating at approximately 1900°F (1040°C) to 1950°F (1065°C) and cooling to room temperature.
How strong is 316L stainless steel?
Mechanical Properties and Yield Strength of 316 / 316L Stainless
| Property | Type 316 (S31600) | Type 316L (S31603) |
|---|---|---|
| Yield Strength 0.2% Offset psi MPa | 30,000 205 | 25,000 170 |
| Ultimate Tensile Strength psi MPa | 75,000 515 | 70,000 485 |
| Percent Elongation in 2 in. or 51mm | 40.0 | 40.0 |
| Hardness, Max. Brinell RB | 217 95 | 217 95 |