What is the modulus of elasticity of 2014 T6 aluminum?
EN AW / AlCu4SiMg / 2014 / T6 / T651
|Melting Point||640 °C|
|Thermal Expansion||22.8 x 10^-6 /K|
|Modulus of Elasticity||73000 GPa|
|Thermal Conductivity||134 – 135 W/m.K|
What is A356?
A356 aluminum alloy is made up of 92.05% Aluminum, 7% Silicon, 0.35% Magnesium, 0.20% Iron, 0.20% Copper, 0.10% Maganese and 0.10% Zinc. It is lightweight and extremely corrosion resistant like stainless steel. If needed, A356 aluminum can be used as a substitute for aluminum alloy 6061.
What is A356 aluminum?
A356 aluminum casting alloy is a 7% Si, 0.3% Mg alloy with 0.2 Fe (max) and 0.10 Zn (max). A356 aluminum casting alloy can also be used as a substitute for aluminum alloy 6061. It is typically used in the heat-treated condition of T5 and T6 hardness properties.
What is the coefficient of thermal expansion for 2014 t6 aluminum?
Aluminum 2014-T6; 2014-T651
|CTE, linear 68°F||23 µm/m-°C||12.8 µin/in-°F|
|CTE, linear 250°C||24.4 µm/m-°C||13.6 µin/in-°F|
|Specific Heat Capacity||0.88 J/g-°C||0.21 BTU/lb-°F|
What is the Young’s modulus of aluminum in PSI?
about 1.0 × 107 psi
The value of Young’s modulus for aluminum is about 1.0 × 107 psi, or 7.0 × 1010 N/m2.
What is the difference between A356 and 356?
Alloy A356 has greater elongation, higher strength and considerably higher ductility than Alloy 356. A356 has improved mechanical properties because of lower iron content, compared to 356.
What is LM25 alloy?
Aluminium Casting Alloy LM25. This alloy conforms to BS 1490:1988 LM25. Castings are standardised in the cast (M) condition, the precipitation treated (TE) condition, the solution treated and stabilised (TB7) condition and the fully heat treated (TF) condition.
What are the units for coefficient of thermal expansion?
The coefficient of thermal expansion measures the fractional change in size per degree change in temperature at a constant pressure and is expressed in 1/K or K⁻¹ (reciprocal kelvin) .